# SCR FP25001P1 or Thyristor Failure Analysis

Date: 2012-11-30

Categories: [Connector Failure Analysis](https://gideonlabs.com/categories/connector-failure-analysis/index.md), [Failure Analysis](https://gideonlabs.com/categories/failure-analysis/index.md), IC Failure Analysis (Integrated Circuit), [Rectifier Failure Analysis](https://gideonlabs.com/categories/rectifier-failure-analysis/index.md)




Gideon Analytical Laboratories received one [SCR](http://en.wikipedia.org/wiki/Silicon-controlled_rectifier) (silicon-controlled rectifier) module FP25001P1 for failure analysis.

An SCR consists of four layers of alternating [p-](https://en.wikipedia.org/wiki/P-type_semiconductor) and [n-type](https://en.wikipedia.org/wiki/N-type_semiconductor) semiconductor materials, NPNP or PNPN structures. The three P-N junctions are labeled J1, J2 and, J3, for the three terminals. [Silicon](https://en.wikipedia.org/wiki/Silicon) is used as the intrinsic semiconductor, to which the proper [dopants](https://en.wikipedia.org/wiki/Dopant) are added. The junctions are either diffused or alloyed (an alloy is a mixed semiconductor or a mixed metal). The [planar](https://en.wikipedia.org/wiki/Diffusion_transistor#Planar_transistor) construction is used for low-power SCRs (and all the junctions are diffused). The [mesa-type](https://en.wikipedia.org/wiki/Diffusion_transistor#Mesa_transistor) construction is used for high-power SCRs. In this case, junction J2 is obtained by the diffusion method, and then the outer two layers are [alloyed](https://en.wikipedia.org/wiki/Alloy) to it since the PNPN pellet is required to handle large [currents.](https://en.wikipedia.org/wiki/Electric_current) It is properly braced thyristor. The term "thyristor" applies to the larger family of multilayer devices that exhibit bistable state-change behavior, that is, switching either on or off.

The anode terminal of an SCR is connected to the p-type material of a PNPN structure, and the cathode terminal is connected to the n-type layer, while the gate of the SCR is connected to the p-type material nearest to the cathode.

The device was tested and found that the gate was open in relationship to T+ on SCR1. SCR1 had melted solder at the lead frame interconnect of T+. This lead frame has lifted off the cathode surface. This happens when there is internal stress on the lead frame as a result of non-concurrent soldering. This lead was not soldered on the cathode sufficiently. This lead is not "wetted" properly. This is indicative of cold solder joints. The complimentary cathode solder shows a similar lack of "wetting."

Sometimes failure analysis is not complicated; in this case, Gideon Labs was able to find the problem fairly quickly and pinpoint the problem on to the manufacturing vendor. Call Gideon Analytical Laboratories the next time you need failure analysis on SCRs.

![scr Die](https://res.cloudinary.com/dy3wlzuye/image/upload/f_auto,c_scale,w_300/GideonLabs/scr2.jpg 'SCR with interconnects')
![SCR Module](https://res.cloudinary.com/dy3wlzuye/image/upload/f_auto,c_scale,w_300/GideonLabs/scr1.jpg 'SCR Module')
![Cathode Lead](https://res.cloudinary.com/dy3wlzuye/image/upload/f_auto,c_scale,w_300/GideonLabs/scr3.jpg 'Lifted Cathode Lead')
![Poor Solder Wetting](https://res.cloudinary.com/dy3wlzuye/image/upload/f_auto,c_scale,w_300/GideonLabs/scr4.jpg 'Poor Solder Wetting ')